COMPOSITES
General Lamination
COMPOSITESL
General purpose polyester resins, pre-accelerated and thixotropic. It has very good wetting characteristics to fiberglass, can be used by manual or spray methods, moderate exothermic reaction and fast hardness development, with good curing time and roughing times. Designed for a wide variety of processes and products.
PPT-201-10
Unsaturated polyesters, modified terephthalics, preaccelerated, thixotropic, good mechanical properties, moderate residual tack release, comply with FMVSS 302 standard. They are used for the manufacture of fiberglass reinforced parts, where manual or spray molding processes are used.
PPT-201-15
Unsaturated polyesters, modified terephthalics, preaccelerated, thixotropic, good mechanical properties, moderate residual tack release, comply with FMVSS 302 standard. They are used for the manufacture of fiberglass reinforced parts, where manual or spray molding processes are used.
PPT-201-20
Unsaturated polyesters, modified terephthalics, preaccelerated, thixotropic, good mechanical properties, moderate residual tack release, comply with FMVSS 302 standard. They are used for the manufacture of fiberglass reinforced parts, where manual or spray molding processes are used.
PPT–4001
Hybrid, pre-accelerated and thixotropic. Good wetting to mineral loads and fiberglass. Rapid development of hardness. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.
PPT – 4015
Hybrid, pre-accelerated and thixotropic. Good wetting to fiberglass. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.
PPT – 4020
Hybrid, pre-accelerated and thixotropic. Good wetting to fiberglass. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.
PPT – 4032
Hybrid, pre-accelerated and thixotropic. Good wetting to fiberglass. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.
PPT – 5535
Hybrid, pre-accelerated and thixotropic. Good wetting to fiberglass. Rapid development of hardness. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.
PPT – 5536
Designed to have adhesion to acrylic, hybrid, pre-accelerated and thixotropic. Outstanding wetting to mineral loads and fiberglass. Rapid development of hardness. Excellent adhesion to acrylic, validated according to ASTM C-297. ts use is recommended in the manufacture of acrylic tubs and sinks, where manual molding or sprinkling processes are used.
PPT – 5539
Designed to have adhesion to acrylic, hybrid, pre-accelerated and thixotropic. Outstanding wetting to mineral loads and fiberglass. Rapid development of hardness. Excellent adhesion to acrylic, validated according to ASTM C-297. ts use is recommended in the manufacture of acrylic tubs and sinks, where manual molding or sprinkling processes are used.
PPT – 5540
Designed to have adhesion to acrylic, hybrid, pre-accelerated and thixotropic. Outstanding wetting to mineral loads and fiberglass. Rapid development of hardness. Excellent adhesion to acrylic, validated according to ASTM C-297. ts use is recommended in the manufacture of acrylic tubs and sinks, where manual molding or sprinkling processes are used.
PPT – 585
Hybrid, pre-accelerated and thixotropic. Good wetting to fiberglass. Rapid development of hardness. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.
PPT – 5857
Ortaphthalic, pre-accelerated and thixotropic. Good wetting to fiberglass. Moderate release of residual tack. Excellent storage stability. ts use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used; and in repackaging in liters, gallons, buckets.
PPT – 607
Hybrid, pre-accelerated and thixotropic. Good wetting to fiberglass. Rapid development of hardness. No residual tack. Its use is recommended in the manufacture of fiberglass reinforced parts, where manual molding or sprinkling processes are used.